Oxidation Resistance of ZrB2 Based Ultra-High Temperature Ceramics
Автор:Fei Peng Год: 2010 Издание:LAP Lambert Academic Publishing Страниц: 112 ISBN: 9783843379892 Specimens of ZrB2 containing various concentrations of SiC, TaB2, and TaSi2 were pressureless-sintered and post-HIPed to theoretical densities. Oxidation resistances were studied by scanning thermogravimetry over the range 1150 - 1550 C, and isothermal thermogravimetry at 1200 - 1900 C. Most silicon-containing compositions formed a glassy surface layer, covering an interior oxide layer. This interior layer was less porous in tantalum-containing compositions. Small concentrations of TaB2 additions were more effective at increasing oxidation resistance than equal additions of TaSi2. The benefit of these additives was related to the formation of fine particles of ZrO2 and TaC during oxidation. These particles resisted wicking of their liquid/glassy borosilicate encapsulation. With increasing TaB2 or TaSi2 concentration, oxidation resistance degraded. In these cases, zirconia dendrites appeared to grow through the glassy layers, providing conduits for oxygen migration. At 1700 C and...